Multi-piece solid golf ball

ABSTRACT

A multi-piece solid golf ball comprising a core, an envelope layer encasing the core, an intermediate layer encasing the envelope layer, and a cover which encases the intermediate layer and has formed on a surface thereof a plurality of dimples, wherein the core is made primarily of a rubber material and has a diameter of at least 31 mm, the envelope layer and intermediate layer are each made primarily of the same or different resin materials and the cover is made primarily of polyurethane; intermediate layer and cover have an optimized thickness relationship; the core, envelope layer, intermediate layer and cover have optimized hardness relationships; and the core surface and core center have a large hardness difference therebetween. The golf ball has excellent flight performance and controllability acceptable to professionals and other skilled golfers, while also having excellent durability to cracking upon repeated impact and excellent scuff resistance.

CROSS REFERENCE TO RELATED APPLICATION

This application is a continuation-in-part of copending application Ser.No. 11/965,441 filed on Dec. 27, 2007, which is a continuation ofapplication Ser. No. 11/518,955 filed Sep. 12, 2006, issued as U.S. Pat.No. 7,335,115, the entire contents of each of which are herebyincorporated by reference.

BACKGROUND OF THE INVENTION

The present invention relates to a multi-piece solid golf ball composedof a core, an envelope layer, an intermediate layer and a cover thathave been formed as successive layers. More specifically, the inventionrelates to a multi-piece solid golf ball for professionals and otherskilled golfers which is endowed with an excellent flight performanceand good controllability.

A variety of golf balls have hitherto been developed for professionalsand other skilled golfers. Of these, multi-piece solid golf balls inwhich the hardness relationship between an intermediate layer encasingthe core and the cover layer has been optimized are in wide use becausethey achieve both a superior distance in the high head speed range andgood controllability on shots taken with an iron and on approach shots.Another important concern is the proper selection of thicknesses andhardnesses for the respective layers of the golf ball in order tooptimize not only flight performance, but also the feel of the ball whenplayed and the spin rate of the ball after being struck with the club,particularly given the large influence of the spin rate on control ofthe ball. A further key concern in ball development, arising from thedesire that golf balls also have durability under repeated impact andscuff resistance against burr formation on the surface of the ball whenrepeatedly played with different types of clubs, is how best to protectthe ball from external factors.

The three-piece solid golf balls having an outer cover layer formedprimarily of a thermoplastic polyurethane which are disclosed in U.S.Pat. No. 6,592,470, U.S. Pat. No. 6,679,791, U.S. Pat. No. 6,533,683,U.S. Pat. No. 6,814,676, U.S. Pat. No. 6,663,507 and U.S. Pat. No.6,702,694 were intended to meet such a need. However, because this golfball does not have a sufficiently reduced spin rate when hit with adriver, it is often unable to deliver a distance that is acceptable toprofessionals and other skilled golfers.

Meanwhile, efforts to improve the flight and other performancecharacteristics of golf balls have led to the development of ballshaving a four-layer construction, i.e., a core encased by threeintermediate or cover layers, that allows the ball construction to bevaried among the several layers at the interior. Such golf balls havebeen disclosed in, for example, JP-A 9-248351, JP-A 10-127818, JP-A10-127819, JP-A 10-295852, JP-A 10-328325, JP-A 10-328326, JP-A10-328327, JP-A 10-328328, JP-A 11-4916 and JP-A 2004-180822.

Yet, as golf balls for the skilled golfer, the above balls provide apoor balance of distance and controllability or fall short in terms ofachieving a lower spin rate on shots with a driver, thus limiting thedegree to which the total distance can be increased. Moreover, withthese golf balls, it has been difficult to achieve in the same ball agood spin rate-lowering effect, good rebound and good durability.

SUMMARY OF THE INVENTION

It is therefore an object of the present invention to provide amulti-piece solid golf ball which has a flight performance andcontrollability that are fully acceptable to professionals and otherskilled golfers, while also having an excellent durability to crackingon repeated impact and an excellent scuff resistance.

The present invention employs, as the basic construction in golf balldesign, an outermost layer made of polyurethane and a multilayerstructure of three or more outer layers (envelope layer/intermediatelayer/cover) encasing the core. By making the cover of polyurethane,which is relatively soft, a spin performance on approach shots that isacceptable to professionals and other skilled golfers and a high scuffresistance can be obtained. By making the envelope layer of a materialcomposed primarily of a specific resin mixture, a lower spin rate onshots with a number one wood (W#1) and a good durability on repeatedimpact are obtained. Moreover, by designing a ball in which the envelopelayer, the intermediate layer and the cover have thicknesses whichsatisfy the relationshipcover thickness<intermediate layer thickness,and the core, envelope layer, intermediate layer and cover have hardnessrelationships which satisfy the following three conditions:core surface hardness≦envelope layer surface hardness  (1)cover material hardness<intermediate layer material hardness  (2)core surface hardness−core center hardness (JIS-C)≧11,  (3)the ball can be imparted with a lower spin rate on full shots with adriver or iron, enabling a good distance to be achieved that isacceptable to professionals and other skilled golfers, in addition towhich the ball can be imparted with an excellent controllability in theshort game.

In other words, the golf ball of the invention, when used byprofessionals and other skilled golfers, is able to resolve theabove-described problems in the prior art due to the synergistic effectsof the materials making up the respective layers of the ball and thehardness relationships therebetween. That is, the golf ball of theinvention provides a fully acceptable flight performance andcontrollability, in addition to which it exhibits an excellentdurability to cracking on repeated impact and excellent scuffresistance, effects which were entirely unanticipated. The inventors,having thus found that the technical challenges recited above can beovercome by the foregoing arrangement, ultimately arrived at the presentinvention.

Accordingly, the invention provides the following multi-piece solid golfballs.

[1] A multi-piece solid golf ball comprising a core, an envelope layerencasing the core, an intermediate layer encasing the envelope layer,and a cover which encases the intermediate layer and has formed on asurface thereof a plurality of dimples, wherein the core is madeprimarily of a rubber material and has a diameter of at least 31 mm, theenvelope layer and intermediate layer are each made primarily of thesame or different resin materials and the cover is made primarily ofpolyurethane, the material hardness of the cover is softer than thematerial hardness of the intermediate layer by the hardness differenceof at least 1 but less than 40 in Durometer D hardness units; theenvelope layer, intermediate layer and cover have thicknesses whichsatisfy the relationshipcover thickness<intermediate layer thickness;and the core, envelope layer, intermediate layer and cover have hardnessrelationships which satisfy the following three conditions:core surface hardness≦envelope layer surface hardness,  (1)cover material hardness<intermediate layer material hardness, and  (2)core surface hardness−core center hardness (JIS-C)≧11.  (3)[2] The multi-piece solid golf ball of [1] above, wherein the core,envelope layer, intermediate layer and cover have hardnesses whichsatisfy the relationshipcore surface hardness≦envelope layer surface hardness<intermediate layermaterial hardness>cover material hardness.[3] The multi-piece solid golf ball of [1], wherein the resin materialmaking up the envelope layer is a mixture comprising, in admixture,

a base resin of (a) an olefin-unsaturated carboxylic acid randomcopolymer and/or a metal ion neutralization product of anolefin-unsaturated carboxylic acid random copolymer mixed with (b) anolefin-unsaturated carboxylic acid-unsaturated carboxylic acid esterternary random copolymer and/or a metal ion neutralization product of anolefin-unsaturated carboxylic acid-unsaturated carboxylic acid esterternary random copolymer in a weight ratio between 100:0 and 0:100, and

(e) a non-ionomeric thermoplastic elastomer in a weight ratio between100:0 and 50:50.

[4] The multi-piece solid golf ball of [1] above, wherein the resinmaterial making up the envelope layer is a mixture comprising:

-   -   100 parts by weight of a resin component composed of, in        admixture,        -   a base resin of (a) an olefin-unsaturated carboxylic acid            random copolymer and/or a metal ion neutralization product            of an olefin-unsaturated carboxylic acid random copolymer            mixed with (b) an olefin-unsaturated carboxylic            acid-unsaturated carboxylic acid ester ternary random            copolymer and/or a metal ion neutralization product of an            olefin-unsaturated carboxylic acid-unsaturated carboxylic            acid ester ternary random copolymer in a weight ratio            between 100:0 and 0:100, and        -   (e) a non-ionomeric thermoplastic elastomer in a weight            ratio between 100:0 and 50:50;

(c) 5 to 80 parts by weight of a fatty acid and/or fatty acid derivativehaving a molecular weight of 280 to 1500; and

(d) 0.1 to 10 parts by weight of a basic inorganic metal compoundcapable of neutralizing un-neutralized acid groups in the base resin andcomponent (c).

[5] The multi-piece solid golf ball of [1] above, wherein the resinmaterial making up the cover is a material composed primarily of aheated mixture of

(A) a thermoplastic polyurethane material, and

(B) an isocyanate mixture of (b-1) an isocyanate compound having atleast two isocyanate groups as functional groups per molecule, dispersedin (b-2) a thermoplastic resin which is substantially non-reactive withisocyanate.

[6] The multi-piece solid golf ball of [1] above, wherein the corematerial is composed of, in admixture, a rubber base, sulfur and anorganosulfur compound.

[7] The multi-piece solid golf ball of [1] above, wherein the envelopelayer, intermediate layer and cover have thicknesses which satisfy therelationship:cover thickness<intermediate layer thickness≦envelope layer thickness.[8] The multi-piece solid golf ball of [1] above, wherein the core hashardness which satisfy the relationshipcore surface hardness−core center hardness (JIS-C)≧15.[9] The multi-piece solid golf ball of [8] above, wherein the core hashardness which satisfy the relationshipcore surface hardness−core center hardness (JIS-C)≧20.[10] The multi-piece solid golf ball of [1] above, wherein the diameterof the core is 31 to 34.96 mm.[11] The multi-piece solid golf ball of [1] above, wherein the number ofthe dimples is at least 280 but not more than 360.[12] The multi-piece solid golf ball of [1] above, wherein the number ofthe dimples is at least 300 but not more than 350.[13] The multi-piece solid golf ball of [1] above, wherein the diameterof the dimples is set to at least 2.5 mm but not more than 6.5 mm.[14] The multi-piece solid golf ball of [1] above, wherein the depth ofthe dimples is set to at least 0.08 mm but not more than 0.30 mm.[15] The multi-piece solid golf ball of [1] above, wherein the dimplecoverage on the spherical surface of the golf ball, which is the sum ofthe individual dimple surface areas, each defined by the border of theflat plane circumscribed by the edge of a dimple, expressed as a ratio(SR) with respect to the spherical surface area of the ball were it tobe free of dimples, is at least 60% but not more than 90%.[16] The multi-piece solid golf ball of [1] above, wherein the value V0obtained by dividing the spatial volume of each dimple below the flatplane circumscribed by the edge of that dimple by the volume of acylinder whose base is the flat plane and whose height from the base tothe maximum depth of the dimple is at least 0.35 but more than 0.80.[17] The multi-piece solid golf ball of [1] above, wherein the VR value,which is the sum of the volumes of individual dimples formed below flatplanes circumscribed by the dimple edges, as a percentage of the volumeof the ball sphere were it to have no dimples thereon, is at least 0.6%but not more than 1.0%.[18] The multi-piece solid golf ball of [1] above, wherein theintermediate layer material is composed primarily of, in admixture, botha zinc-neutralized ionomer resin and a sodium-neutralized ionomer resinin which the mixing ratio, expressed as the weight ratio ofzinc-neutralized resin to sodium-neutralized resin is from 25/75 to75/25.[19] A multi-piece solid golf ball comprising a core, an envelope layerencasing the core, an intermediate layer encasing the envelope layer,and a cover which encases the intermediate layer and has formed on asurface thereof a plurality of dimples, wherein the core is madeprimarily of a rubber material and has a diameter of at least 31 mm, theenvelope layer and intermediate layer are each made primarily of thesame or different resin materials and the cover is made primarily ofpolyurethane, the material hardness of the cover is softer than thematerial hardness of the intermediate layer by the hardness differenceof at least 1 but less than 40 in Durometer D hardness units; theenvelope layer, intermediate layer and cover have thicknesses whichsatisfy the relationshipcover thickness<intermediate layer thickness≦envelope layer thickness;and the core, envelope layer, intermediate layer and cover have hardnessrelationships which satisfy the following three conditions:cover material hardness<intermediate layer material hardness, and  (2)core surface hardness−core center hardness (JIS-C)≧11.  (3)[20] The multi-piece solid golf ball of [19] above, wherein the resinmaterial making up the envelope layer is a mixture comprising, inadmixture,

a base resin of (a) an olefin-unsaturated carboxylic acid randomcopolymer and/or a metal ion neutralization product of anolefin-unsaturated carboxylic acid random copolymer mixed with (b) anolefin-unsaturated carboxylic acid-unsaturated carboxylic acid esterternary random copolymer and/or a metal ion neutralization product of anolefin-unsaturated carboxylic acid-unsaturated carboxylic acid esterternary random copolymer in a weight ratio between 100:0 and 0:100, and

(e) a non-ionomeric thermoplastic elastomer in a weight ratio between100:0 and 50:50.

[21] The multi-piece solid golf ball of [19] above, wherein the resinmaterial making up the envelope layer is a mixture comprising:

-   -   100 parts by weight of a resin component composed of, in        admixture,        -   a base resin of (a) an olefin-unsaturated carboxylic acid            random copolymer and/or a metal ion neutralization product            of an olefin-unsaturated carboxylic acid random copolymer            mixed with (b) an olefin-unsaturated carboxylic            acid-unsaturated carboxylic acid ester ternary random            copolymer and/or a metal ion neutralization product of an            olefin-unsaturated carboxylic acid-unsaturated carboxylic            acid ester ternary random copolymer in a weight ratio            between 100:0 and 0:100, and        -   (e) a non-ionomeric thermoplastic elastomer in a weight            ratio between 100:0 and 50:50;

(c) 5 to 80 parts by weight of a fatty acid and/or fatty acid derivativehaving a molecular weight of 280 to 1500; and

(d) 0.1 to 10 parts by weight of a basic inorganic metal compoundcapable of neutralizing un-neutralized acid groups in the base resin andcomponent (c).

[22] The multi-piece solid golf ball of [19] above, wherein the resinmaterial making up the cover is a material composed primarily of aheated mixture of

(A) a thermoplastic polyurethane material, and

(B) an isocyanate mixture of (b-1) an isocyanate compound having atleast two isocyanate groups as functional groups per molecule, dispersedin (b-2) a thermoplastic resin which is substantially non-reactive withisocyanate.

[23] The multi-piece solid golf ball of [19] above, wherein the corematerial is composed of, in admixture, a rubber base, sulfur and anorganosulfur compound.

[24] The multi-piece solid golf ball of [19] above, wherein the core hashardness which satisfy the relationshipcore surface hardness−core center hardness (JIS-C)≧15.[25] The multi-piece solid golf ball of [19] above, wherein the core hashardness which satisfy the relationshipcore surface hardness−core center hardness (JIS-C)≧20.[26] The multi-piece solid golf ball of [19] above, wherein the core andenvelope layer have hardnesses which satisfy the relationshipcore surface hardness≦envelope layer surface hardness.[27] The multi-piece solid golf ball of [19] above, wherein the diameterof the core is 31 to 34.96 mm.[28] The multi-piece solid golf ball of [19] above, wherein the numberof the dimples is at least 300 but not more than 350; the diameter ofthe dimples is set to at least 2.5 mm but not more than 6.5 mm; thedepth of the dimples is set to at least 0.08 mm but not more than 0.30mm; the dimple coverage on the spherical surface of the golf ball, whichis the sum of the individual dimple surface areas, each defined by theborder of the flat plane circumscribed by the edge of a dimple,expressed as a ratio (SR) with respect to the spherical surface area ofthe ball were it to be free of dimples, is at least 60% but not morethan 90%; the value V0 obtained by dividing the spatial volume of eachdimple below the flat plane circumscribed by the edge of that dimple bythe volume of a cylinder whose base is the flat plane and whose heightfrom the base to the maximum depth of the dimple is at least 0.35 butmore than 0.80; the VR value, which is the sum of the volumes ofindividual dimples formed below flat planes circumscribed by the dimpleedges, as a percentage of the volume of the ball sphere were it to haveno dimples thereon, is at least 0.6% but not more than 1.0%.[29] The multi-piece solid golf ball of [19] above, wherein theintermediate layer material is composed primarily of, in admixture, botha zinc-neutralized ionomer resin and a sodium-neutralized ionomer resinin which the mixing ratio, expressed as the weight ratio ofzinc-neutralized resin to sodium-neutralized resin is from 25/75 to75/25.

BRIEF DESCRIPTION OF THE DIAGRAMS

FIG. 1 is a schematic sectional view showing a multi-piece solid golfball (4-layer construction) according to the invention.

FIG. 2 is a top view of a golf ball showing an arrangement of dimplesthat may be used in the embodiments of the invention.

DETAILED DESCRIPTION OF THE INVENTION

The invention is described more fully below. The multi-piece solid golfball of the present invention, as shown in FIG. 1, is a golf ball Ghaving four or more layers, including a core 1, an envelope layer 2encasing the core, an intermediate layer 3 encasing the envelope layer,and a cover 4 encasing the intermediate layer. The cover 4 typically hasa large number of dimples D formed on the surface thereof. The core 1and the intermediate layer 3 are not limited to single layers, and mayeach be formed of a plurality of two more layers.

The core diameter in the invention is not subject to any particularlimitation, but is preferably between 31 mm and 38 mm, more preferablyat least 32.5 mm but not more than 37 mm, and most preferably at least34 mm but not more than 36 mm. A core diameter outside this range willlower the initial velocity of the ball or yield a less than adequatespin rate-lowering effect after the ball is hit, as a result of which anincreased distance may not be achieved.

The center hardness of the core, while not subject to any particularlimitation, preferably has a JIS-C hardness of at least 54 but not morethan 72, more preferably at least 57 but not more than 68, and mostpreferably at least 60 but not more than 65. Below the above range, therebound characteristics of the core may be inadequate, as a result ofwhich an increased distance may not be achieved, and the durability tocracking on repeated impact may worsen. Conversely, at a core centerhardness higher than the above range, the ball may have an excessivelyhard feel on full shots and the spin rate may be too high, as a resultof which an increased distance may not be achieved.

The surface hardness of the core, while not subject to any particularlimitation, preferably has a Durometer D hardness (the value measuredwith a type D durometer based on ASTM D2240; the same applies to theDurometer D hardnesses mentioned below for the respective layers) of atleast 45 but not more than 65, more preferably at least 50 but not morethan 60, and even more preferably at least 52 but not more than 58.Below the above range, the rebound characteristics of the core may beinadequate, as a result of which an increased distance may not beachieved, and the durability to cracking on repeated impact may worsen.Conversely, at a core surface hardness higher than the above range, theball may have an excessively hard feel on full shots with a driver andthe spin rate may be too high, as a result of which an increaseddistance may not be achieved.

In the practice of the invention, it is critical that the core have asurface hardness which is higher than the hardness at the center of thecore, with the difference therebetween being at least 11 JIS-C units,preferably at least 15 JIS-C units, and more preferably at least 20JIS-C units. If the difference is too small, the spin rate-loweringeffect on full shots with a driver or the like may be insufficient,causing the ball to describe a high trajectory, as a result of which anincreased distance may not be achieved.

The deflection of the core when subjected to loading, i.e., thedeflection of the core when compressed from an initial load of 98 N (10kgf) to a final load of 1,275 N (130 kgf), while not subject to anyparticular limitation, is preferably set within a range of 2.0 mm to 5.0mm, more preferably 2.3 mm to 4.5 mm, and even more preferably 2.6 mm to4.0 mm. If this value is too high, the core may lack sufficient rebound,which may result in a less than adequate distance, or the durability ofthe ball to cracking on repeated impact may worsen. On the other hand,if this value is too low, the ball may have an excessively hard feel onfull shots with a driver, and the spin rate may be too high, as a resultof which an increased distance may not be achieved.

The core having the above-described surface hardness and deflection ismade primarily of a rubber component. For example, the core may be madeof a rubber composition containing, in addition to the rubber component,a co-crosslinking agent, an organic peroxide, an inert filler, anorganosulfur compound, sulfur (i.e., elemental sulfur) and the like. Itis preferable to use polybutadiene as the base rubber of this rubbercomposition.

It is desirable for the polybutadiene serving as the rubber component tohave a cis-1,4-bond content on the polymer chain of at least 60 wt %,preferably at least 80 wt %, more preferably at least 90 wt %, and mostpreferably at least 95 wt %. Too low a cis-1,4-bond content among thebonds on the molecule may lead to a lower resilience.

Moreover, the polybutadiene has a 1,2-vinyl bond content on the polymerchain of preferably not more than 2%, more preferably not more than1.7%, and even more preferably not more than 1.5%. Too high a 1,2-vinylbond content may lead to a lower resilience.

To obtain a molded and vulcanized rubber composition of good resilience,the polybutadiene used therein is preferably one synthesized with arare-earth catalyst or a Group VIII metal compound catalyst.Polybutadiene synthesized with a rare-earth catalyst is especiallypreferred.

Such rare-earth catalysts are not subject to any particular limitation.Exemplary rare-earth catalysts include those made up of a combination ofa lanthanide series rare-earth compound with an organoaluminum compound,an alumoxane, a halogen-bearing compound and an optional Lewis base.

Examples of suitable lanthanide series rare-earth compounds includehalides, carboxylates, alcoholates, thioalcoholates and amides of atomicnumber 57 to 71 metals.

In the practice of the invention, the use of a neodymium catalyst inwhich a neodymium compound serves as the lanthanide series rare-earthcompound is particularly advantageous because it enables a polybutadienerubber having a high cis-1,4 bond content and a low 1,2-vinyl bondcontent to be obtained at an excellent polymerization activity. Suitableexamples of such rare-earth catalysts include those mentioned in JP-A11-35633, JP-A 11-164912 and JP-A 2002-293996.

To enhance the resilience, it is preferable for the polybutadienesynthesized using the lanthanide series rare-earth compound catalyst toaccount for at least 10 wt %, preferably at least 20 wt %, and morepreferably at least 40 wt %, of the rubber components.

Rubber components other than the above-described polybutadiene may beincluded in the base rubber insofar as the effects of the invention arenot compromised. Illustrative examples of suitable rubber componentsother than the above-described polybutadiene include otherpolybutadienes, and other diene rubbers, such as styrene-butadienerubber, natural rubber, isoprene rubber and ethylene-propylene-dienerubber.

Examples of co-crosslinking agents include unsaturated carboxylic acidsand the metal salts of unsaturated carboxylic acids.

Specific examples of unsaturated carboxylic acids include acrylic acid,methacrylic acid, maleic acid and fumaric acid. Acrylic acid andmethacrylic acid are especially preferred.

The metal salts of unsaturated carboxylic acids, while not subject toany particular limitation, are exemplified by the above-mentionedunsaturated carboxylic acids neutralized with a desired metal ion.Specific examples include the zinc and magnesium salts of methacrylicacid and acrylic acid. The use of zinc acrylate is especially preferred.

The unsaturated carboxylic acid and/or metal salt thereof is included inan amount, per 100 parts by weight of the base rubber, of generally atleast 10 parts by weight, preferably at least 15 parts by weight, andmore preferably at least 20 parts by weight, but generally not more than60 parts by weight, preferably not more than 50 parts by weight, morepreferably not more than 45 parts by weight, and most preferably notmore than 40 parts by weight. Too much may make the core too hard,giving the ball an unpleasant feel on impact, whereas too little maylower the rebound.

The organic peroxide may be a commercially available product, suitableexamples of which include Percumyl D (produced by NOF Corporation),Perhexa 3M (NOF Corporation), and Luperco 231XL (Atochem Co.). These maybe used singly or as a combination of two or more thereof.

The amount of organic peroxide included per 100 parts by weight of thebase rubber is preferably at least 0.1 part by weight, more preferablyat least 0.3 part by weight, even more preferably at least 0.5 part byweight, and most preferably at least 1 part by weight, but preferablynot more than 6 parts by weight, more preferably not more than 5 partsby weight, even more preferably not more than 4 parts by weight, andmost preferably not more than 3 parts by weight. Too much or too littleorganic peroxide may make it impossible to achieve a ball having a goodfeel on impact, durability and rebound.

Examples of suitable inert fillers include zinc oxide, barium sulfateand calcium carbonate. These may be used singly or as a combination oftwo or more thereof.

The amount of inert filler included per 100 parts by weight of the baserubber is preferably at least 1 part by weight, and more preferably atleast 5 parts by weight, but preferably not more than 60 parts byweight, more preferably not more than 50 parts by weight, and even morepreferably not more than 40 parts by weight. Too much or too littleinert filler may make it impossible to achieve a proper weight and agood rebound.

In addition, an antioxidant may be included if necessary. Illustrativeexamples of suitable commercial antioxidants include Nocrac NS-6, NocracNS-30 (both available from Ouchi Shinko Chemical Industry Co., Ltd.),and Yoshinox 425 (available from Yoshitomi Pharmaceutical Industries,Ltd.). These may be used singly or as a combination of two or morethereof.

The amount of antioxidant included per 100 parts by weight of the baserubber is preferably 0 or more part by weight, more preferably at least0.05 part by weight, and even more preferably at least 0.1 part byweight, but preferably not more than 3 parts by weight, more preferablynot more than 2 parts by weight, even more preferably not more than 1part by weight, and most preferably not more than 0.5 part by weight.Too much or too little antioxidant may make it impossible to achieve agood rebound and durability.

To enhance the rebound of the golf ball and increase its initialvelocity, it is preferable to include within the core an organosulfurcompound.

No particular limitation is imposed on the organosulfur compound,provided it improves the rebound of the golf ball. Exemplaryorganosulfur compounds include thiophenols, thionaphthols, halogenatedthiophenols, and metal salts thereof. Specific examples includepentachlorothiophenol, pentafluorothiophenol, pentabromothiophenol,p-chlorothiophenol, the zinc salt of pentachlorothiophenol, the zincsalt of pentafluorothiophenol, the zinc salt of pentabromothiophenol,the zinc salt of p-chlorothiophenol; and diphenylpolysulfides,dibenzylpolysulfides, dibenzoylpolysulfides, dibenzothiazoylpolysulfidesand dithiobenzoylpolysulfides having 2 to 4 sulfurs. Diphenyldisulfideand the zinc salt of pentachlorothiophenol are especially preferred.

It is recommended that the amount of the organosulfur compound includedper 100 parts by weight of the base rubber be preferably at least 0.05part by weight, and more preferably at least 0.1 part by weight, butpreferably not more than 5 parts by weight, more preferably not morethan 4 parts by weight, even more preferably not more than 3 parts byweight, and most preferably not more than 2.5 parts by weight. If toomuch organosulfur compound is included, the effects of addition may peakso that further addition has no apparent effect, whereas the use of toolittle organosulfur compound may fail to confer the effects of suchaddition to a sufficient degree.

It is desirable to include sulfur (elemental sulfur) in the base rubberof which the core is primarily made. The sulfur may be in the form of apowder, such as that produced by Tsurumi Chemical Industry Co., Ltd.under the trade name “Z Sulfur.” The amount of sulfur included per 100parts by weight of the base rubber in the core is preferably at least0.05 part by weight, more preferably at least 0.07 part by weight, andeven more preferably at least 0.09 part by weight, but preferably notmore than 0.5 part by weight, more preferably not more than 0.3 part byweight, and even more preferably not more than 0.2 part by weight. Iftoo little sulfur is included, it may not be possible to achieve atleast a certain minimum hardness difference between the surface of thecore and the center of the core. On the other hand, too much sulfur maylower the rebound resilience and prevent the ball from achieving asufficient distance.

Next, the envelope layer is described.

The envelope layer has a material hardness, expressed as the Durometer Dhardness, which, while not subject to any particular limitation, ispreferably at least 40 but not more than 62, more preferably at least 47but not more than 60, and even more preferably at least 53 but not morethan 58. If the envelope layer material is softer than the above range,the ball may have too much spin receptivity on full shots, as a resultof which an increased distance may not be achieved. On the other hand,if this material is harder than the above range, the durability of theball to cracking under repeated impact may worsen and the ball may havetoo hard a feel when played. The envelope layer has a thickness which,while not subject to any particular limitation, is preferably at least1.0 mm but not more than 4.0 mm, more preferably at least 1.2 mm but notmore than 3.0 mm, and even more preferably at least 1.4 mm but not morethan 2.0 mm. Outside of this range, the spin rate-lowering effect onfull shots with a driver (W#1) or an iron may be inadequate, as a resultof which an increased distance may not be achieved.

The term “material hardness” used above refers to the hardness of theenvelope layer material itself, not the hardness at the surface of thespherical body composed of the core encased by the envelope layer.Specifically, the material hardness is the sheet hardness obtained bymolding the envelope layer material into a sheet of a given thickness asstipulated in a hardness standard, and measuring the hardness of theresulting molded sheet. The same applies to the material hardness of thesubsequently described intermediate layer and cover.

The envelope layer has a surface hardness, expressed as the Durometer Dhardness, which, while not subject to any particular limitation, ispreferably at least 50 but not more than 70, more preferably at least 53but not more than 67, and even more preferably at least 55 but not morethan 63. At a surface hardness lower than this range, the ball may havetoo much spin receptivity on full shots, as a result of which anincreased distance may not be achieved. On the other hand, if thesurface hardness is higher than the above range, the durability of theball to cracking under repeated impact may worsen and the ball may havetoo hard a feel when played. Although not subject to any particularlimitation, it is preferable for the surface of the envelope layer to besofter than the surface of the intermediate layer. While no particularlimitation is imposed on the degree to which it is softer (hardnessdifference), the difference in Durometer D hardness is preferably atleast 3 but not more than 25, more preferably at least 5 but not morethan 18, and even more preferably at least 7 but not more than 15.Outside of this range, if the surface of the envelope layer is too muchsofter than the surface of the intermediate layer, the rebound of theball may decrease or the spin rate may become excessive, as a result ofwhich an increased distance may not be achieved.

It is critical for the surface of the envelope layer to be as hard as orharder than the surface of the core. The hardness difference between thesurface of the envelope layer and the surface of the core, expressed interms of Durometer D hardness, is preferably at least 0 but not morethan 12, more preferably at least 0 but not more than 10, and even morepreferably at least 0 but not more than 8. If the surface of theenvelope layer is instead softer than the core surface, the spinrate-lowering effect on shots with a driver will be inadequate, as aresult of which an increased distance will not be achieved. Conversely,if the surface of the envelope layer is too much harder than the coresurface, the feel of the ball on full shots may be too hard and thedurability of the ball to cracking on repeated impact may worsen.

The envelope layer in the invention is made primarily of a resinmaterial. The resin material of the envelope layer, while not subject toany particular limitation, is preferably one which includes as anessential component a base resin of (a) an olefin-unsaturated carboxylicacid random copolymer and/or a metal ion neutralization product of anolefin-unsaturated carboxylic acid random copolymer mixed in a specificratio with (b) an olefin-unsaturated carboxylic acid-unsaturatedcarboxylic acid ester ternary random copolymer and/or a metal ionneutralization product of an olefin-unsaturated carboxylicacid-unsaturated carboxylic acid ester ternary random copolymer.

The olefin in the above base resin, for either component (a) orcomponent (b), has a number of carbons which is generally at least 2 butnot more than 8, and preferably not more than 6. Specific examplesinclude ethylene, propylene, butene, pentene, hexene, heptene andoctene. Ethylene is especially preferred.

Examples of unsaturated carboxylic acids include acrylic acid,methacrylic acid, maleic acid and fumaric acid. Acrylic acid andmethacrylic acid are especially preferred.

Moreover, the unsaturated carboxylic acid ester is preferably a loweralkyl ester of the above unsaturated carboxylic acid. Specific examplesinclude methyl methacrylate, ethyl methacrylate, propyl methacrylate,butyl methacrylate, methyl acrylate, ethyl acrylate, propyl acrylate andbutyl acrylate. Butyl acrylate (n-butyl acrylate, i-butyl acrylate) isespecially preferred.

The olefin-unsaturated carboxylic acid random copolymer of component (a)and the olefin-unsaturated carboxylic acid-unsaturated carboxylic acidester ternary random copolymer of component (b) (the copolymers incomponents (a) and (b) are referred to collectively below as “the randomcopolymers”) can each be obtained by preparing the above-mentionedmaterials and carrying out random copolymerization by a known method.

It is recommended that the above random copolymers have controlledcontents of unsaturated carboxylic acid (acid contents). Here, it isrecommended that the content of unsaturated carboxylic acid present inthe random copolymer serving as component (a) is generally at least 4 wt%, preferably at least 6 wt %, more preferably at least 8 wt %, and evenmore preferably at least 10 wt %, but not more than 30 wt %, preferablynot more than 20 wt %, even more preferably not more than 18 wt %, andmost preferably not more than 15 wt %.

Similarly, it is recommended that the content of unsaturated carboxylicacid present in the random copolymer serving as component (b) isgenerally at least 4 wt %, preferably at least 6 wt %, and morepreferably at least 8 wt %, but not more than 15 wt %, preferably notmore than 12 wt %, and even more preferably not more than 10 wt %. Ifthe acid content of the random copolymer is too low, the rebound maydecrease, whereas if it is too high, the processability of the envelopelayer-forming resin material may decrease.

The metal ion neutralization product of an olefin-unsaturated carboxylicacid random copolymer of component (a) and the metal ion neutralizationproduct of an olefin-unsaturated carboxylic acid-unsaturated carboxylicacid ester ternary random copolymer of component (b) (the metal ionneutralization products of the copolymers in components (a) and (b) arereferred to collectively below as “the metal ion neutralization productsof the random copolymers”) can be obtained by neutralizing some of theacid groups on the random copolymers with metal ions.

Illustrative examples of metal ions for neutralizing the acid groupsinclude Na⁺, K⁺, Li⁺, Zn⁺⁺, Cu⁺⁺, Mg⁺⁺, Ca⁺⁺, Co⁺⁺, Ni⁺⁺ and Pb⁺⁺. Ofthese, preferred use can be made of, for example, Na⁺, Li⁺, Zn⁺⁺ andMg⁺⁺. To improve resilience, the use of Na⁺ is even more preferred.

The above metal ion neutralization products of the random copolymers maybe obtained by neutralizing the random copolymers with the foregoingmetal ions. For example, use may be made of a method in whichneutralization is carried out with a compound such as a formate,acetate, nitrate, carbonate, hydrogencarbonate, oxide, hydroxide oralkoxide of the above-mentioned metal ions. No particular limitation isimposed on the degree of neutralization of the random copolymer by thesemetal ions.

Sodium ion-neutralized ionomer resins may be suitably used as the abovemetal ion neutralization products of the random copolymers to increasethe melt flow rate of the material. This facilitates adjustment to thesubsequently described optimal melt flow rate, enabling the moldabilityto be improved.

Commercially available products may be used as the base resins of abovecomponents (a) and (b). Illustrative examples of the random copolymer incomponent (a) include Nucrel 1560, Nucrel 1214 and Nucrel 1035 (allproducts of DuPont-Mitsui Polychemicals Co., Ltd.), and Escor 5200,Escor 5100 and Escor 5000 (all products of ExxonMobil Chemical).Illustrative examples of the random copolymer in component (b) includeNucrel AN 4311 and Nucrel AN 4318 (both products of DuPont-MitsuiPolychemicals Co., Ltd.), and Escor ATX325, Escor ATX320 and EscorATX310 (all products of ExxonMobil Chemical).

Illustrative examples of the metal ion neutralization product of therandom copolymer in component (a) include Himilan 1554, Himilan 1557,Himilan 1601, Himilan 1605, Himilan 1706 and Himilan AM7311 (allproducts of DuPont-Mitsui Polychemicals Co., Ltd.), Surlyn 7930 (E.I.DuPont de Nemours & Co.), and Iotek 3110 and Iotek 4200 (both productsof ExxonMobil Chemical). Illustrative examples of the metal ionneutralization product of the random copolymer in component (b) includeHimilan 1855, Himilan 1856 and Himilan AM7316 (all products ofDuPont-Mitsui Polychemicals Co., Ltd.), Surlyn 6320, Surlyn 8320, Surlyn9320 and Surlyn 8120 (all products of E.I. DuPont de Nemours & Co.), andIotek 7510 and Iotek 7520 (both products of ExxonMobil Chemical).Sodium-neutralized ionomer resins that are suitable as the metal ionneutralization product of the random copolymer include Himilan 1605,Himilan 1601 and Himilan 1555.

When preparing the above-described base resin, component (a) andcomponent (b) must be admixed in a weight ratio of generally between100:0 and 0:100, preferably between 100:0 and 25:75, more preferablybetween 100:0 and 50:50, even more preferably between 100:0 and 75:25,and most preferably 100:0. If too little component (a) is included, themolded material obtained therefrom may have a decreased resilience.

In addition, the processability of the base resin can be furtherimproved by also adjusting the ratio in which the random copolymers andthe metal ion neutralization products of the random copolymers areadmixed when preparing the base resin as described above. It isrecommended that the weight ratio of the random copolymer to the metalion neutralization product of the random copolymer be generally between0:100 and 60:40, preferably between 0:100 and 40:60, more preferablybetween 0:100 and 20:80, and most preferably 0:100. The addition of toomuch random copolymer may lower the processability during mixing.

Component (e) described below may be added to the base resin. Component(e) is a non-ionomeric thermoplastic elastomer. The purpose of thiscomponent is to further improve the feel of the ball on impact and therebound. Examples include olefin elastomers, styrene elastomers,polyester elastomers, urethane elastomers and polyamide elastomers. Tofurther increase the rebound, it is preferable to use a polyesterelastomer or an olefin elastomer. The use of an olefin elastomercomposed of a thermoplastic block copolymer which includes crystallinepolyethylene blocks as the hard segments is especially preferred.

A commercially available product may be used as component (e).Illustrative examples include Dynaron (JSR Corporation) and thepolyester elastomer Hytrel (DuPont-Toray Co., Ltd.).

It is recommended that component (e) be included in an amount, per 100parts by weight of the base resin of the invention, of generally atleast 0 part by weight, preferably at least 5 parts by weight, morepreferably at least 10 parts by weight, and most preferably at least 20parts by weight, but not more than 100 parts by weight, preferably notmore than 60 parts by weight, more preferably not more than 50 parts byweight, and most preferably not more than 40 parts by weight. Too muchcomponent (e) will lower the compatibility of the mixture, possiblyresulting in a substantial decline in the durability of the golf ball.

Next, component (c) described below may be added to the base resin.Component (c) is a fatty acid or fatty acid derivative having amolecular weight of at least 280 but not more than 1500. Compared withthe base resin, this component has a very low molecular weight and, bysuitably adjusting the melt viscosity of the mixture, helps inparticular to improve the flow properties. Component (c) includes arelatively high content of acid groups (or derivatives), and is capableof suppressing an excessive loss in resilience.

The fatty acid or fatty acid derivative of component (c) has a molecularweight of at least 280, preferably at least 300, more preferably atleast 330, and even more preferably at least 360, but not more than1,500, preferably not more than 1,000, even more preferably not morethan 600, and most preferably not more than 500. If the molecular weightis too low, the heat resistance cannot be improved. On the other hand,if the molecular weight is too high, the flow properties cannot beimproved.

The fatty acid or fatty acid derivative of component (c) may be anunsaturated fatty acid (or derivative thereof) containing a double bondor triple bond on the alkyl moiety, or it may be a saturated fatty acid(or derivative thereof) in which the bonds on the alkyl moiety are allsingle bonds. It is recommended that the number of carbons on themolecule be preferably at least 18, more preferably at least 20, evenmore preferably at least 22, and most preferably at least 24, but notmore than 80, preferably not more than 60, more preferably not more than40, and even more preferably not more than 30. Too few carbons may makeit impossible to improve the heat resistance and may also make the acidgroup content so high as to diminish the flow-improving effect due tointeractions with acid groups present in the base resin. On the otherhand, too many carbons increases the molecular weight, as a result ofwhich a distinct flow-improving effect may not appear.

Specific examples of the fatty acid of component (c) include stearicacid, 1,2-hydroxystearic acid, behenic acid, oleic acid, linoleic acid,linolenic acid, arachidic acid and lignoceric acid. Of these, stearicacid, arachidic acid, behenic acid and lignoceric acid are preferred.Behenic acid is especially preferred.

The fatty acid derivative of component (c) is exemplified by metallicsoaps in which the proton on the acid group of the fatty acid has beenreplaced with a metal ion. Examples of the metal ion include Na⁺, Li⁺,Ca⁺⁺, Mg⁺⁺, Zn⁺⁺, Mn⁺⁺, Al⁺⁺⁺, Ni⁺⁺, Fe⁺⁺, Fe⁺⁺⁺, Cu⁺⁺, Sn⁺⁺, Pb⁺⁺ andCo⁺⁺. Of these, Ca⁺⁺, Mg⁺⁺ and Zn⁺⁺ are especially preferred.

Specific examples of fatty acid derivatives that may be used ascomponent (c) include magnesium stearate, calcium stearate, zincstearate, magnesium 1,2-hydroxystearate, calcium 1,2-hydroxystearate,zinc 1,2-hydroxystearate, magnesium arachidate, calcium arachidate, zincarachidate, magnesium behenate, calcium behenate, zinc behenate,magnesium lignocerate, calcium lignocerate and zinc lignocerate. Ofthese, magnesium stearate, calcium stearate, zinc stearate, magnesiumarachidate, calcium arachidate, zinc arachidate, magnesium behenate,calcium behenate, zinc behenate, magnesium lignocerate, calciumlignocerate and zinc lignocerate are preferred.

Component (d) may be added as a basic inorganic metal compound capableof neutralizing acid groups in the base resin and in component (c). Ifcomponent (d) is not included, when a metallic soap-modified ionomerresin (e.g., the metallic soap-modified ionomer resins cited in theabove-mentioned patent publications) is used alone, the metallic soapand un-neutralized acid groups present on the ionomer resin undergoexchange reactions during mixture under heating, generating a largeamount of fatty acid. Because the fatty acid has a low thermal stabilityand readily vaporizes during molding, it may cause molding defects.Moreover, if the fatty acid thus generated deposits on the surface ofthe molded material, it may substantially lower paint film adhesion andmay have other undesirable effects such as lowering the resilience ofthe resulting molded material.

To solve this problem, the envelope layer-forming resin material mayinclude also, as an essential component, a basic inorganic metalcompound (d) which neutralizes the acid groups present in the base resinand component (c), in this way improving the resilience of the moldedmaterial.

That is, by including component (d) as an essential ingredient in thematerial, not only are the acid groups in the base resin and component(c) neutralized, through synergistic effects from the proper addition ofeach of these components it is possible as well to increase the thermalstability of the mixture and thus confer a good moldability, and also toenhance the resilience.

Here, it is recommended that the basic inorganic metal compound used ascomponent (d) be a compound having a high reactivity with the base resinand containing no organic acids in the reaction by-products, enablingthe degree of neutralization of the mixture to be increased without aloss of thermal stability.

Illustrative examples of the metal ions in the basic inorganic metalcompound serving as component (d) include Li⁺, Na⁺, K⁺, Ca⁺⁺, Mg⁺⁺,Zn⁺⁺, Al⁺⁺⁺, Ni⁺⁺, Fe⁺⁺, Fe⁺⁺⁺, Cu⁺⁺, Mn⁺⁺, Sn⁺⁺, Pb⁺⁺ and Co⁺⁺. Knownbasic inorganic fillers containing these metal ions may be used as thebasic inorganic metal compound. Specific examples include magnesiumoxide, magnesium hydroxide, magnesium carbonate, zinc oxide, sodiumhydroxide, sodium carbonate, calcium oxide, calcium hydroxide, lithiumhydroxide and lithium carbonate. In particular, a hydroxide or amonoxide is recommended. Calcium hydroxide and magnesium oxide, whichhave a high reactivity with the base resin, are more preferred. Calciumhydroxide is especially preferred.

Because the above-described resin material is arrived at by blendingspecific respective amounts of components (c) and (d) with the resincomponent, i.e., the base resin containing specific respective amountsof components (a) and (b) in combination with optional component (e),this material has excellent thermal stability, flow properties andmoldability, and can impart the molded material with a markedly improvedresilience.

Components (c) and (d) are included in respective amounts, per 100 partsby weight of the resin component suitably formulated from components(a), (b) and (e), of at least 5 parts by weight, preferably at least 10parts by weight, more preferably at least 15 parts by weight, and evenmore preferably at least 18 parts by weight, but not more than 80 partsby weight, preferably not more than 40 parts by weight, more preferablynot more than 25 parts by weight, and even more preferably not more than22 parts by weight, of component (c); and at least 0.1 part by weight,preferably at least 0.5 part by weight, more preferably at least 1 partby weight, and even more preferably at least 2 parts by weight, but notmore than 10 parts by weight, preferably not more than 8 parts byweight, more preferably not more than 6 parts by weight, and even morepreferably not more than 5 parts by weight, of component (d). Too littlecomponent (c) lowers the melt viscosity, resulting in inferiorprocessability, whereas too much lowers the durability. Too littlecomponent (d) fails to improve thermal stability and resilience, whereastoo much instead lowers the heat resistance of the golf ball-formingmaterial due to the presence of excess basic inorganic metal compound.

In the above-described resin material formulated from the respectiveabove-indicated amounts of the resin component and components (c) and(d), it is recommended that at least 50 mol %, preferably at least 60mol %, more preferably at least 70 mol %, and even more preferably atleast 80 mol %, of the acid groups be neutralized. Such a high degree ofneutralization makes it possible to more reliably suppress the exchangereactions that cause trouble when only a base resin and a fatty acid orfatty acid derivative are used as in the above-cited prior art, thuspreventing the generation of fatty acid. As a result, there is obtaineda resin material of substantially improved thermal stability and goodprocessability which can provide molded products of much betterresilience than prior-art ionomer resins.

“Degree of neutralization,” as used above, refers to the degree ofneutralization of acid groups present within the mixture of the baseresin and the fatty acid or fatty acid derivative serving as component(c), and differs from the degree of neutralization of the ionomer resinitself when an ionomer resin is used as the metal ion neutralizationproduct of a random copolymer in the base resin. A mixture according tothe invention having a certain degree of neutralization, when comparedwith an ionomer resin alone having the same degree of neutralization,contains a very large number of metal ions. This large number of metalions increases the density of ionic crosslinks which contribute toimproved resilience, making it possible to confer the molded productwith excellent resilience.

To more reliably achieve a material having both a high degree ofneutralization and good flow properties, it is recommended that the acidgroups in the above-described mixture be neutralized with transitionmetal ions and with alkali metal and/or alkaline earth metal ions.Although neutralization with transition metal ions provides a weakerionic cohesion than neutralization with alkali metal and alkaline earthmetal ions, the combined use of these different types of ions toneutralize acid groups in the mixture can substantially improve the flowproperties.

It is recommended that the molar ratio between the transition metal ionsand the alkali metal and/or alkaline earth metal ions be in a range oftypically 10:90 to 90:10, preferably 20:80 to 80:20, more preferably30:70 to 70:30, and most preferably 40:60 to 60:40. Too low a molarratio of transition metal ions may fail to provide a sufficientflow-improving effect. On the other hand, too high a transition metalion molar ratio may lower the resilience.

Examples of the metal ions include, but are not limited to, zinc ions asthe transition metal ions and at least one type of ion selected fromamong sodium, lithium and magnesium ions as the alkali metal or alkalineearth metal ions.

A known method may be used to obtain a mixture in which the desiredamount of acid groups have been neutralized with transition metal ionsand alkali metal or alkaline earth metal ions. Specific examples ofmethods of neutralization with transition metal ions, particularly zincions, include methods which use zinc soaps as the fatty acid derivative,methods which use zinc ion neutralization products (e.g., a zincion-neutralized ionomer resin) when formulating components (a) and (b)as the base resin, and methods which use zinc compounds such as zincoxide as the basic inorganic metal compound of component (d).

The resin material should preferably have a melt flow rate adjusted toensure flow properties that are particularly suitable for injectionmolding, and thus improve moldability. Specifically, it is recommendedthat the melt flow rate (MFR), as measured according to JIS K7210 at atest temperature of 190° C. and under a load of 21.18 N (2.16 kgf), beset to generally at least 0.5 dg/min, preferably at least 1 dg/min, morepreferably at least 1.5 dg/min, and even more preferably at least 2dg/min, but generally not more than 20 dg/min, preferably not more than10 dg/min, more preferably not more than 5 dg/min, and even morepreferably not more than 3 dg/min. Too high or low a melt flow rate mayresult in a substantial decline in processability.

Next, the intermediate layer is described.

The material from which the intermediate layer is formed has a hardness,expressed as the Durometer D hardness, which, while not subject to anyparticular limitation, is preferably at least 50 but not more than 70,more preferably at least 55 but not more than 66, and even morepreferably at least 60 but not more than 63. If the intermediate layermaterial is softer than the above range, the ball may have too much spinreceptivity on full shots, as a result of which an increased distancemay not be attained. On the other hand, if this material is harder thanthe above range, the durability of the ball to cracking under repeatedimpact may worsen and the ball may have too hard a feel when played witha putter or on short approach shots. The intermediate layer has athickness which, while not subject to any particular limitation, ispreferably at least 0.7 mm but not more than 2.0 mm, more preferably atleast 0.9 mm but not more than 1.7 mm, and even more preferably at least1.1 mm but not more than 1.4 mm. Outside of this range, the spinrate-lowering effect on shots with a driver (W#1) may be inadequate, asa result of which an increased distance may not be achieved. Moreover, athickness lower than the above range may worsen the durability tocracking on repeated impact or the low-temperature durability.

The intermediate layer may be made primarily of a resin material whichis the same as or different from the above-described material used toform the envelope layer. An ionomer resin is especially preferred.Specific examples include sodium-neutralized ionomer resins availableunder the trade name designations Himilan 1605, Himilan 1601 and Surlyn8120, and zinc-neutralized ionomer resins such as Himilan 1557 andHimilan 1706. These may be used singly or as a combination of two ormore thereof.

An embodiment in which the intermediate layer material is composedprimarily of, in admixture, both a zinc-neutralized ionomer resin and asodium-neutralized ionomer resin is especially preferable for attainingthe objects of the invention. The mixing ratio, expressed as the weightratio of zinc-neutralized resin to sodium-neutralized resin, isgenerally from 25/75 to 75/25, preferably from 35/65 to 65/35, and morepreferably from 45/55 to 55/45.

Outside of this range, the ball rebound may be too low, as a result ofwhich the desired distance may not be achieved, the durability torepeated impact at normal temperature may worsen, and the durability tocracking at low temperatures (below 0° C.) may worsen.

The surface hardness of the intermediate layer, i.e., the surfacehardness of the sphere composed of the core and the envelope layerenclosed by the intermediate layer, while not subject to any particularlimitation, has a Durometer D hardness of preferably at least 60 but notmore than 80, more preferably at least 63 but not more than 77, and evenmore preferably at least 67 but not more than 73. If the surface of theintermediate layer is softer than the above range, the ball may have toomuch spin receptivity on full shots, as a result of which an increaseddistance may not be achieved. On the other hand, if it is harder thanthe above range, the durability of the ball to cracking under repeatedimpact may worsen and the ball may have too hard a feel when played witha putter or on short approach shots.

To increase adhesion between the intermediate layer material and thepolyurethane used in the subsequently described cover, it is desirableto abrade the surface of the intermediate layer. In addition, it ispreferable to apply a primer (adhesive) to the surface of theintermediate layer following such abrasion or to add an adhesionreinforcing agent to the intermediate layer material. Examples ofadhesion reinforcing agents that may be incorporated in the intermediatelayer material include organic compounds such as 1,3-butanediol andtrimethylolpropane, and oligomers such as polyethylene glycol andpolyhydroxy polyolefin oligomers. The use of trimethylolpropane or apolyhydroxy polyolefin oligomer is especially preferred. Examples ofcommercially available products include trimethylolpropane produced byMitsubishi Gas Chemical Co., Ltd. and polyhydroxy polyolefin oligomersproduced by Mitsubishi Chemical Corporation (under the trade namedesignation Polytail H; number of main-chain carbons, 150 to 200; withhydroxyl groups at the ends).

Next, the cover is described. As used herein, the term “cover” denotesthe outermost layer of the ball construction, and excludes what isreferred to herein as the intermediate layer and the envelope layer.

The cover material has a hardness, expressed as the Durometer Dhardness, which, while not subject to any particular limitation, ispreferably at least 40 but not more than 60, more preferably at least 43but nor more than 57, and even more preferably at least 46 but not morethan 54. At a hardness below this range, the ball tends to take on toomuch spin on full shots, as a result of which an increased distance maynot be achieved. On the other hand, at a hardness above this range, onapproach shots, the ball lacks spin receptivity and thus may have aninadequate controllability even when played by a professional or otherskilled golfer.

It is critical for the material hardness of the cover to be softer thanthe material hardness of the intermediate layer. The hardness differencebetween the intermediate layer material and the cover material,expressed in Durometer D hardness units, is preferably at least 1 butless than 40, more preferably at least 3 but less than 30, and even morepreferably at least 6 but less than 20. If this difference is too small,the spin rate-lowering effect on full shots with a driver or an iron maybe inadequate, as a result of which the desired distance may not beachieved.

The thickness of the cover, while not subject to any particularlimitation, is preferably at least 0.3 mm but not more than 1.5 mm, morepreferably at least 0.5 mm but not more than 1.3 mm, and even morepreferably at least 0.7 mm but not more than 1.1 mm. If the cover isthicker than the above range, the ball may have an inadequate rebound onshots with a driver (W#1) or the spin rate may be too high, as a resultof which an increased distance may not be achieved. Conversely, if thecover is thinner than the above range, the ball may have a poor scuffresistance and inadequate controllability even when played by aprofessional or other skilled golfer.

In the practice of the invention, the cover material is composedprimarily of polyurethane, thereby enabling the intended effects of theinvention, i.e., both a good controllability and a good scuffresistance, to be achieved.

The polyurethane used as the cover material, while not subject to anyparticular limitation, is preferably a thermoplastic polyurethane,particularly from the standpoint of amenability to mass production. Inthe practice of the invention, it is preferable to use a cover-moldingmaterial

(C) composed primarily of components A and B below:

(A) a thermoplastic polyurethane material;

(B) an isocyanate mixture of (b-1) an isocyanate compound having atleast two isocyanate groups as functional groups per molecule, dispersedin (b-2) a thermoplastic resin which is substantially non-reactive withisocyanate.

Components A, B and C are described below.

(A) Thermoplastic Polyurethane Material

The thermoplastic polyurethane material has a morphology which includessoft segments composed of a polymeric polyol (polymeric glycol) and hardsegments composed of a chain extender and a diisocyanate. The polymericpolyol used as a starting material may be any that is employed in theart relating to thermoplastic polyurethane materials, without particularlimitation. Exemplary polymeric polyols include polyester polyols andpolyether polyols, although polyether polyols are better than polyesterpolyols for synthesizing thermoplastic polyurethane materials thatprovide a high rebound resilience and have excellent low-temperatureproperties. Suitable polyether polyols include polytetramethylene glycoland polypropylene glycol. Polytetramethylene glycol is especiallypreferred for achieving a good rebound resilience and goodlow-temperature properties. The polymeric polyol has an averagemolecular weight of preferably 1,000 to 5,000. To synthesize athermoplastic polyurethane material having a high rebound resilience, anaverage molecular weight of 2,000 to 4,000 is especially preferred.

Preferred chain extenders include those used in the prior art relatingto thermoplastic polyurethane materials. Illustrative, non-limiting,examples include 1,4-butylene glycol, 1,2-ethylene glycol,1,3-butanediol, 1,6-hexanediol, and 2,2-dimethyl-1,3-propanediol. Thesechain extenders have an average molecular weight of preferably 20 to15,000.

Diisocyanates suitable for use include those employed in the prior artrelating to thermoplastic polyurethane materials. Illustrative,non-limiting, examples include aromatic diisocyanates such as4,4′-diphenylmethane diisocyanate, 2,4-toluene diisocyanate and2,6-toluene diisocyanate; and aliphatic diisocyanates such ashexamethylene diisocyanate. Depending on the type of isocyanate used,the crosslinking reaction during injection molding may be difficult tocontrol. In the present invention, to ensure stable reactivity with thesubsequently described isocyanate mixture (B), it is most preferable touse an aromatic diisocyanate, and specifically 4,4′-diphenylmethanediisocyanate.

A commercial product may be suitably used as the above-describedthermoplastic polyurethane material. Illustrative examples includePandex T-8290, Pandex T-8295 and Pandex T-8260 (all manufactured by DICBayer Polymer, Ltd.), and Resamine 2593 and Resamine 2597 (bothmanufactured by Dainichi Seika Colour & Chemicals Mfg. Co., Ltd.).

(B) Isocyanate Mixture

The isocyanate mixture (B) is prepared by dispersing (b-1) an isocyanatecompound having as functional groups at least two isocyanate groups permolecule in (b-2) a thermoplastic resin that is substantiallynon-reactive with isocyanate. Above isocyanate compound (b-1) ispreferably an isocyanate compound used in the prior art relating tothermoplastic polyurethane materials. Illustrative, non-limiting,examples include aromatic diisocyanates such as 4,4′-diphenylmethanediisocyanate, 2,4-toluene diisocyanate and 2,6-toluene diisocyanate; andaliphatic diisocyanates such as hexamethylene diisocyanate. From thestandpoint of reactivity and work safety, the use of4,4′-diphenylmethane diisocyanate is most preferred.

The thermoplastic resin (b-2) is preferably a resin having a low waterabsorption and excellent compatibility with thermoplastic polyurethanematerials. Illustrative, non-limiting, examples of such resins includepolystyrene resins, polyvinyl chloride resins, ABS resins, polycarbonateresins and polyester elastomers (e.g., polyether-ester block copolymers,polyester-ester block copolymers). From the standpoint of reboundresilience and strength, the use of a polyester elastomer, particularlya polyether-ester block copolymer, is especially preferred.

In the isocyanate mixture (B), it is desirable for the relativeproportions of the thermoplastic resin (b-2) and the isocyanate compound(b-1), expressed as the weight ratio (b-2):(b-1), to be from 100:5 to100:100, and especially from 100:10 to 100:40. If the amount of theisocyanate compound (b-1) relative to the thermoplastic resin (b-2) istoo small, a greater amount of the isocyanate mixture (B) will have tobe added to achieve an amount of addition sufficient for thecrosslinking reaction with the thermoplastic polyurethane material (A).As a result, the thermoplastic resin (b-2) will exert a large influence,compromising the physical properties of the cover-molding material (C).On the other hand, if the amount of the isocyanate compound (b-1)relative to the thermoplastic resin (b-2) is too large, the isocyanatecompound (b-1) may cause slippage to occur during mixing, makingpreparation of the isocyanate mixture (B) difficult.

The isocyanate mixture (B) can be obtained by, for example, adding theisocyanate compound (b-1) to the thermoplastic resin (b-2) andthoroughly working together these components at a temperature of 130 to250° C. using mixing rolls or a Banbury mixer, then either pelletizingor cooling and subsequently grinding. A commercial product such asCrossnate EM30 (made by Dainichi Seika Colour & Chemicals Mfg. Co.,Ltd.) may be suitably used as the isocyanate mixture (B).

(C) Cover-Molding Material

The cover-molding material (C) is composed primarily of theabove-described thermoplastic polyurethane material (A) and isocyanatemixture (B). The relative proportion of the thermoplastic polyurethanematerial (A) to the isocyanate mixture (B) in the cover-molding material(C), expressed as the weight ratio A:B, is preferably from 100:1 to100:100, more preferably from 100:5 to 100:50, and even more preferablyfrom 100:10 to 100:30. If too little isocyanate mixture (B) is includedwith respect to the thermoplastic polyurethane material (A), asufficient crosslinking effect will not be achieved. On the other hand,if too much is included, unreacted isocyanate may discolor the moldedmaterial.

In addition to the above-described ingredients, other ingredients may beincluded in the cover-molding material (C). For example, thermoplasticpolymeric materials other than the thermoplastic polyurethane materialmay be included; illustrative examples include polyester elastomers,polyamide elastomers, ionomer resins, styrene block elastomers,polyethylene and nylon resins. Thermoplastic polymeric materials otherthan the thermoplastic polyurethane material may be included in anamount of 0 to 100 parts by weight, preferably 1 to 75 parts by weight,and more preferably 10 to 50 parts by weight, per 100 parts by weight ofthe thermoplastic polyurethane material serving as the essentialcomponent. The amount of such thermoplastic polymeric materials used isselected as appropriate for such purposes as adjusting the hardness ofthe cover material, improving the rebound, improving the flowproperties, and improving adhesion. If necessary, various additives suchas pigments, dispersants, antioxidants, light stabilizers, ultravioletabsorbers and parting agents may also be suitably included in thecover-molding material (C).

Formation of the cover from the cover-molding material (C) can becarried out by adding the isocyanate mixture (B) to the thermoplasticpolyurethane material (A) and dry mixing, then using an injectionmolding machine to mold the mixture into a cover over the core. Themolding temperature varies with the type of thermoplastic polyurethanematerial (A), although molding is generally carried out within atemperature range of 150 to 250° C.

Reactions and crosslinking which take place in the golf ball coverobtained as described above are believed to involve the reaction ofisocyanate groups with hydroxyl groups remaining on the thermoplasticpolyurethane material to form urethane bonds, or the creation of anallophanate or biuret crosslinked form via a reaction involving theaddition of isocyanate groups to urethane groups in the thermoplasticpolyurethane material. Although the crosslinking reaction has not yetproceeded to a sufficient degree immediately after injection molding ofthe cover-molding material (C), the crosslinking reaction can be made toproceed further by carrying out an annealing step after molding, in thisway conferring the golf ball cover with useful characteristics.“Annealing,” as used herein, refers to heat aging the cover at aconstant temperature for a given length of time, or aging the cover fora fixed period at room temperature.

In the addition to the above resin components, various optionaladditives may be included in the above-described resin materials for theenvelope layer, the intermediate layer and the cover. Such additivesinclude, for example, pigments, dispersants, antioxidants, ultravioletabsorbers, ultraviolet stabilizers, parting agents, plasticizers, andinorganic fillers (e.g., zinc oxide, barium sulfate, titanium dioxide).

Thickness Relationship Between Envelope Layer, Intermediate Layer andCover

In the practice of the invention, it is not subject to any particularlimitation, but the relationship between the thicknesses of the envelopelayer, the intermediate layer and the cover preferably satisfy thefollowing conditions:cover thickness<intermediate layer thickness.In particular, it is more preferable for the following conditions to besatisfied:cover thickness<intermediate layer thickness≦envelope layer thickness.That is, with regard to the distribution in the thicknesses of therespective layers of the ball, by setting the core diameter to at least31 mm and designing the ball such that the thicknesses of the layersbecome gradually smaller in the order of the above conditions, there canbe obtained a ball which achieves a good flight performance,controllability, durability and feel on impact. Should the cover bethicker than the intermediate layer, the ball rebound may decrease orthe ball may have excessive spin receptivity on full shots, as a resultof which an increased distance may not be attainable. Should theenvelope layer be thinner than the intermediate layer, the spinrate-lowering effect may be inadequate, possibly preventing the desireddistance from being achieved.Hardness Relationship Between Envelope Layer, Intermediate Layer andCover

In the practice of the invention, in addition to optimizing thethickness relationship among the above respective layers, it is notsubject to any particular limitation, but the relationship between thehardnesses of the respective layers preferably satisfy the followingconditions:core surface hardness≦envelope layer surface hardness, and  (1)cover material hardness<intermediate layer material hardness.  (2)In particular, it is preferable for the following conditions to besatisfied:core surface hardness≦envelope layer surface hardness<intermediate layermaterial hardness>cover material hardness.The technical significance of this hardness relationship is as relatedabove in the descriptions of the respective members.

With regard to the hardness of the core, it is critical that thefollowing relationship be satisfied:core surface hardness−core center hardness (JIS-C)≧11.  (3)The technical significance of this is also as described above.

The multi-piece solid golf ball of the invention can be manufacturedusing an ordinary process such as a known injection molding process toform on top of one another the respective layers described above: thecore, envelope layer, intermediate layer, and cover. For example, amolded and vulcanized article composed primarily of the core materialmay be placed as the core within a particular injection-molding mold,following which the envelope layer-forming material and the intermediatelayer-forming material may be injection-molded in this order to give anintermediate spherical body. The spherical body may then be placedwithin another injection-molding mold and the cover material injectionmolded over the spherical body to give a multi-piece golf ball.Alternatively, the cover may be formed as a layer over the intermediatespherical body by, for example, placing two half-cups, molded beforehandas hemispherical shells, around the intermediate spherical body so as toencase it, then molding under applied heat and pressure.

Numerous dimples may be formed on the surface of the cover. The dimplesarranged on the cover surface, while not subject to any particularlimitation, number preferably at least 280 but not more than 360, morepreferably at least 300 but not more than 350, and even more preferablyat least 320 but not more than 340. If the number of dimples is higherthan the above range, the ball will tend to have a low trajectory, whichmay shorten the distance of travel. On the other hand, if the number ofdimples is too small, the ball will tend to have a high trajectory, as aresult of which an increased distance may not be achieved.

Any one or combination of two or more dimple shapes, including circularshapes, various polygonal shapes, dewdrop shapes and oval shapes, may besuitably used. If circular dimples are used, the diameter of the dimplesmay be set to at least about 2.5 mm but not more than about 6.5 mm, andthe depth may be set to at least 0.08 mm but not more than 0.30 mm.

To fully manifest the aerodynamic characteristics of the dimples, thedimple coverage on the spherical surface of the golf ball, which is thesum of the individual dimple surface areas, each defined by the borderof the flat plane circumscribed by the edge of the dimple, expressed asa ratio (SR) with respect to the spherical surface area of the ball wereit to be free of dimples, is preferably at least 60% but not more than90%. Also, to optimize the trajectory of the ball, the value V0 obtainedby dividing the spatial volume of each dimple below the flat planecircumscribed by the edge of that dimple by the volume of a cylinderwhose base is the flat plane and whose height from the base to themaximum depth of the dimple is preferably at least 0.35 but not morethan 0.80. In addition, the VR value, which is the sum of the volumes ofindividual dimples formed below flat planes circumscribed by the dimpleedges, as a percentage of the volume of the ball sphere were it to haveno dimples thereon, is preferably at least 0.6% but not more than 1.0%.Outside of the above ranges for these values, the ball may assume atrajectory that is not conducive to achieving a good distance, as aresult of which the ball may fail to travel a sufficient distance whenplayed.

The golf ball of the invention, which can be manufactured so as toconform with the Rules of Golf for competitive play, may be produced toa ball diameter which is of a size that will not pass through a ringhaving an inside diameter of 42.672 mm, yet is not more than 42.80 mm,and to a weight of generally from 45.0 to 45.93 g.

As shown above, by using a specific resin mixture as the envelope layer,by using primarily a polyurethane material in the cover, by optimizingthe hardnesses of the core, envelope layer, intermediate layer andcover, and by making the difference in hardness between the surface ofthe core and the center of the core large, the golf ball according tothe invention is highly beneficial for professionals and other skilledgolfers because it lowers the spin rate of the ball on full shots takenwith a driver or an iron, thus providing an increased distance and goodcontrollability, and because it has an excellent durability to crackingunder repeated impact and an excellent scuff resistance.

EXAMPLES

Examples of the invention and Comparative Examples are given below byway of illustration, and not by way of limitation.

Examples 1 and 2, Comparative Examples 1 to 6 Formation of Core

Rubber compositions were formulated as shown in Table 1, then molded andvulcanized under the conditions shown in Table 1 to form cores. InComparative Example 4, the rubber composition shown in Table 1 wasprepared and vulcanized, following which the resulting center core wasencased by the outer core layer (envelope layer) shown in Table 2 in anunvulcanized state, and the resulting sphere was molded and vulcanizedto give a layered construction.

TABLE 1 Example Comparative Example (parts by weight) 1 2 1 2 3 4 5 6Core Polybutadiene A 0 0 0 0 0 0 0 100 formulation Polybutadiene B 80 8080 80 80 80 80 0 Polybutadiene C 20 20 20 20 20 20 20 0 Zinc acrylate34.2 31.0 34.2 34.2 31.0 34.2 40.6 25.7 Peroxide (1) 0 0 0 0 0 0 0 0.6Peroxide (2) 3 3 3 3 3 3 3 0.6 Antioxidant (1) 0.1 0.1 0.1 0.1 0.1 0.10.1 0 Antioxidant (2) 0 0 0 0 0 0 0 0.1 Zinc oxide 28.0 29.2 37.0 70.031.0 17.0 16.1 33.1 Zinc salt of 1.5 1.5 1.5 1.5 1.5 1.5 1.5 0.3pentachlorothiophenol Sulfur 0.1 0.1 0.1 0.1 0.1 0.1 0.1 0 Zinc stearate5 5 5 5 5 5 5 5 Vulcanization Temperature (° C.) 155 155 155 155 155 155155 155 conditions Time (min) 15 15 15 15 15 15 15 15

Trade names for some the materials appearing in the table are givenbelow.

Polybutadiene A

Available from JSR Corporation under the trade name BR01.

Polybutadiene B

Available from JSR Corporation under the trade name BR730.

Polybutadiene C

Available from JSR Corporation under the trade name BR51.

Peroxide 1

Dicumyl peroxide, available from NOF Corporation under the trade namePercumyl D.

Peroxide 2

A mixture of 1,1-di(t-butylperoxy)cyclohexane and silica, available fromNOF Corporation under the trade name Perhexa C-40.

Antioxidant (1)

2,6-di-t-butyl-4-methylphenol, produced by Ouchi Shinko ChemicalIndustry Co., Ltd. under the trade name Nocrac 200.

Antioxidant (2)

2,2′-methylenebis(4-methyl-6-t-butylphenol), produced by Ouchi ShinkoChemical Industry Co., Ltd. under the trade name Nocrac NS-6.

Sulfur

Available from Tsurumi Chemical Industry Co., Ltd. under the trade nameZ Sulfur.

TABLE 2 Comparative (parts by weight) Example 4 Core formulationPolybutadiene B 100 Zinc acrylate 46.6 Peroxide (2) 2 Antioxidant (2) 0Zinc oxide 11.0 Zinc salt of pentachlorothiophenol 1.5 Zinc stearate 5Vulcanization Temperature (° C.) 155 conditions Time (min) 15 Note:Details concerning the above materials are the same as in Table 1.Formation of Envelope Layer, Intermediate Layer and Cover

Next, the envelope layer, intermediate layer and cover formulated fromthe various resin components shown in Table 3 were injection-molded,thereby forming over the core, in order, an envelope layer, anintermediate layer and a cover. In Comparative Example 4, the rubbermaterial mentioned above was used as the envelope layer. Next, thedimples shown in Table 4, which were common to all the examples, wereformed on the cover surface, thereby producing multi-piece solid golfballs.

TABLE 3 Formulation (pbw) No. 1 No. 2 No. 3 No. 4 No. 5 No. 6 Himilan1605 68.75 50 Himilan 1557 30 15 Himilan 1706 35 Himilan 1855 20 AM731150 Surlyn 8120 75 AN4311 Dynaron E6100P 31.25 25 Behenic acid 18 20Calcium hydroxide 2.3 2.3 Calcium stearate 0.15 0.15 Zinc stearate 0.150.15 Trimethylolpropane 1.1 Polytail H 2 Pandex T-8295 100 Pandex T-8260100 Titanium oxide 2.2 3.8 3.8 Polyethylene 1.4 1.4 Isocyanate compound18 18

Trade names for some the materials appearing in the table are givenbelow.

-   Himilan: An ionomer resin produced by DuPont-Mitsui Polychemicals    Co., Ltd.-   Surlyn: An ionomer resin produced by E.I. DuPont de Nemours & Co.-   AM7311: An ionomer resin produced by DuPont-Mitsui Polychemicals    Co., Ltd.-   AN4311: Nucrel, produced by DuPont-Mitsui Polychemicals Co., Ltd.-   Dynaron E6100P: A hydrogenated polymer produced by JSR Corporation.    Hytrel: A polyester elastomer produced by DuPont-Toray Co., Ltd.-   Behenic acid: NAA222-S (beads), produced by NOF Corporation.-   Calcium hydroxide: CLS-B, produced by Shiraishi Kogyo.-   Polytail H: A low-molecular-weight polyolefin polyol produced by    Mitsubishi Chemical Corporation.-   Pandex: MDI-PTMG type thermoplastic polyurethane produced by DIC    Bayer Polymer.-   Isocyanate compound: Crossnate EM30, an isocyanate masterbatch which    is produced by Dainichi Seika Colour & Chemicals Mfg. Co., Ltd.,    contains 300 of 4,4′-diphenylmethane diisocyanate (measured    concentration of amine reverse-titrated isocyanate according to JIS    K1556, 5 to 100), and in which the masterbatch base resin is a    polyester elastomer. The isocyanate compound was mixed with Pandex    at the time of injection molding.

TABLE 4 Number of Diameter Depth No. dimples (mm) (mm) V₀ SR VR 1 12 4.60.15 0.47 0.81 0.783 2 234 4.4 0.15 0.47 3 60 3.8 0.14 0.47 4 6 3.5 0.130.46 5 6 3.4 0.13 0.46 6 12 2.6 0.10 0.46 Total 330 Dimple DefinitionsDiameter: Diameter of flat plane circumscribed by edge of dimple. Depth:Maximum depth of dimple from flat plane circumscribed by edge of dimple.V₀: Spatial volume of dimple below flat plane circumscribed by dimpleedge, divided by volume of cylinder whose base is the flat plane andwhose height is the maximum depth of dimple from the base. SR: Sum ofindividual dimple surface areas, each defined by the border of the flatplane circumscribed by the edge of the dimple, as a percentage ofsurface area of ball sphere were it to have no dimples thereon. VR: Sumof volumes of individual dimples formed below flat plane circumscribedby the edge of the dimple, as a percentage of volume of ball sphere wereit to have no dimples thereon.

The golf balls obtained in Examples 1 and 2 the invention and inComparative Examples 1 to 6 were tested and evaluated according to thecriteria described below with regard to the following: surface hardnessand other physical properties of each layer and of the ball, flightperformance, spin rate on approach shots (controllability), durabilityto repeated impact, and scuff resistance. The results are shown in Table5. All measurements were carried out in a 23° C. environment.

(1) Core Deflection

The core was placed on a hard plate, and the deflection (mm) by the corewhen compressed under a final load of 1,275 N (130 kgf) from an initialload of 98 N (10 kgf) was measured.

(2) Core Center Hardness

The core was cut into hemispheres, the cut face was prepared as a flatplane, and measurement was carried out by pressing the durometerindenter perpendicularly against the cut face. The results are indicatedas JIS-C hardness values.

(3-i) Core Surface Hardness (Measured as JIS-C Hardness)

The durometer was set substantially perpendicular to the surface portionof the spherical core, and the hardness was measured in accordance withthe JIS-C hardness standard. The results are indicated as JIS-C hardnessvalues.

The hardness difference between the surface of the core and the centerof the core was obtained by subtracting the hardness value at the centerof the core from the hardness value at the core surface obtained bymeasurement according to the JIS-C standard.

(3-ii) Core Surface Hardness (Measured as D Hardness)

Although the core surface is spherical, the durometer indenter was setsubstantially perpendicular to this spherical surface and Durometer Dhardness measurements (using a type D durometer in accordance with ASTMD2240) were taken at two randomly selected points on the surface of thecore. The average of the two measurements was used as the core surfacehardness.

(4) Hardness of Envelope Layer Material

The resin material for the envelope layer was formed into a sheet havinga thickness of about 2 mm, and the hardness was measured with a type Ddurometer in accordance with ASTM D2240.

(5) Surface Hardness of Envelope Layer-Covered Sphere

The durometer indenter was set substantially perpendicular to thespherical surface of the envelope layer, and measurements were taken inaccordance with ASTM D2240.

(6) Hardness of Intermediate Layer Material

The resin material used in the intermediate layer was formed into a 2 mmthick sheet. After at least two weeks had elapsed, the hardness of thesheet was measured with a type D durometer in accordance with ASTMD2240.

(7) Surface Hardness of Intermediate Layer-Covered Sphere

The durometer indenter was set substantially perpendicular to thespherical surface of the intermediate layer, and measurements were takenin accordance with ASTM D2240.

(8) Hardness of Cover Material

The same method of measurement was used as in (6) above.

(9) Flight Performance

The carry and total distance of the ball when hit at a head speed (HS)of 45 m/s with a club (TourStage X-Drive Type 405, manufactured byBridgestone Sports Co., Ltd.; loft angle, 9.5° mounted on a swing robotwere measured. The results were rated according to the criteriaindicated below. The spin rate was the value measured for the ballimmediately following impact with an apparatus for measuring initialconditions.

Good: Total distance was 232.0 m or more

NG: Total distance was less than 232.0 m

(10) Spin Rate on Approach Shots

The spin rate of a ball hit at a head speed of 22 m/s with a sand wedge(abbreviated below as “SW”; J's Classical Edition, manufactured byBridgestone Sports Co., Ltd.) was measured. The results were ratedaccording to the criteria indicated below. The spin rate was measured bythe same method as that used above when measuring distance.

-   -   Good: Spin rate of 6,600 rpm or more    -   Fair: Spin rate of at least 6,300 rpm but less than 6,600 rpm    -   NG: Spin rate of less than 6,300 rpm        (11) Durability to Repeated Impact

The ball was repeatedly hit at a head speed of 40 m/s with a W#1 clubmounted on a golf swing robot. The number of shots that had been takenwith the ball in Example 2 when the initial velocity fell below 97% ofthe average initial velocity for the first 10 shots was assigned adurability index of “100”, and similarly obtained durability indices forthe balls in each example were evaluated according to the followingcriteria. The average value for N=3 balls was used as the basis forevaluation in each example.

Good: Durability index was 90 or more

NG: Durability index was less than 90

(12) Scuff Resistance

A non-plated pitching sand wedge was set in a swing robot, and the ballwas hit once at a head speed of 40 m/s, following which the surfacestate of the ball was visually examined and rated as follows.

Good: Can be used again

NG: Cannot be used again

TABLE 5 Example Comparative Example 1 2 1 2 3 4 5 6 Core Diameter (mm)34.96 34.92 34.96 29.04 34.96 34.96 37.30 34.96 Weight (g) 27.46 27.4028.50 18.51 27.63 25.86 31.86 27.46 Deflection (mm) 3.5 3.8 3.5 3.5 3.83.5 3.0 3.5 Surface hardness 84 81 84 84 81 84 89 74 (JIS-C) Centerhardness 63 61 63 63 61 63 63 64 (JIS-C) Surface - center 21 20 21 21 2021 26 10 (JIS-C) Surface hardness 56 53 56 56 53 56 59 48 (Shore D)Envelope Type No. 1 No. 1 No. 1 No. 1 No. 2 Rubber — No. 1 layercomposition Thickness (mm) 1.68 1.69 1.67 4.08 1.67 1.67 — 1.67 Specificgravity 0.93 0.93 0.93 0.93 0.93 1.16 — 0.93 Material hardness 56 56 5656 51 — — 56 (Shore D) Sphere¹⁾ Surface hardness 61 61 61 61 56 60 — 61(Shore D) Diameter (mm) 38.3 38.3 38.3 37.2 38.3 38.3 — 38.3 Weight (g)34.1 34.0 35.1 31.7 34.2 34.0 — 34.0 Intermediate Type No. 4 No. 4 No. 4No. 4 No. 1 No. 4 No. 4 No. 4 layer Thickness (mm) 1.17 1.17 1.18 1.731.18 1.18 1.68 1.18 Specific gravity 0.96 0.96 0.96 0.96 0.93 0.96 0.960.96 Material hardness 62 62 62 62 56 62 62 62 (Shore D) Sphere²⁾Surface hardness 70 70 70 70 61 70 70 70 (Shore D) Diameter (mm) 40.6540.65 40.65 40.65 40.65 40.65 40.65 40.65 Weight (g) 39.5 39.5 40.6 39.539.5 39.5 39.5 39.5 Cover Type No. 5 No. 5 No. 3 No. 5 No. 6 No. 5 No. 5No. 5 Thickness (mm) 1.03 1.02 0.96 1.03 1.03 1.03 1.03 1.03 Specificgravity 1.15 1.15 0.96 1.15 1.15 1.15 1.15 1.15 Material hardness 53 5353 53 58 53 53 53 (D) Ball Diameter (mm) 42.7 42.7 42.7 42.7 42.7 42.742.7 42.7 Weight (g) 45.5 45.5 45.5 45.5 45.5 45.5 45.5 45.5 Flight W#1Spin (rpm) 2760 2696 2735 2980 2625 2808 2798 2782 performance (HS,Carry (m) 221.3 220.8 220.1 219.5 219.5 220.5 221.0 220.8 45 m/s) Total236.9 234.1 235.1 229.5 232.1 234.3 230.5 230.8 distance (m) Rating goodgood good NG good good NG NG SW Spin rate 6946 6796 6524 6975 6026 69666813 6856 (HS, (rpm) 22 m/s) Rating good good fair good NG good goodgood Durability to repeated impact good good good good good NG good goodScuff resistance good good NG good NG good good good ¹⁾Sphere composedof core covered by envelope layer. ²⁾Sphere composed of core covered byenvelope layer and intermediate layer.

As is apparent from the results in Table 5, in Comparative Example 1,the cover material was an ionomer and thus had a low scuff resistance.In Comparative Example 2, the core diameter was less than 31 mm; whenthe ball was hit with a number one wood (W#1), the spin rate was highand thus an increase in distance was not achieved. In ComparativeExample 3, the cover was harder than the intermediate layer, as a resultof which the ball was not receptive to spin on approach shots. InComparative Example 4, the envelope layer material was rubber; the ballthus had a low durability to repeated impact. The ball in ComparativeExample 5 was a three-piece golf ball composed of a core enclosed by twolayers and lacking an envelope layer; because the spin rate was high,there was no increase in distance. In Comparative Example 6, thehardness difference between the core surface and the center of the corewas less than 11 JIS-C units. Hence, the ball had a high spin rate whenhit with a W#1, as a result of which an increased distance was notachieved.

The invention claimed is:
 1. A multi-piece solid golf ball comprising acore, an envelope layer encasing the core, an intermediate layerencasing the envelope layer, and a cover which encases the intermediatelayer and has formed on a surface thereof a plurality of dimples,wherein the core is made primarily of a rubber material and has adiameter of at least 31 mm, the envelope layer and intermediate layerare each made primarily of the same or different resin materials and thecover is made primarily of polyurethane, the material hardness of thecover is softer than the material hardness of the intermediate layer bythe hardness difference of at least 1 but less than 40 in Durometer Dhardness units; the envelope layer, intermediate layer and cover havethicknesses which satisfy the relationshipcover thickness<intermediate layer thickness; and the core, envelopelayer, intermediate layer and cover have hardness relationships whichsatisfy the following three conditions:core surface hardness≦envelope layer surface hardness,  (1)cover material hardness<intermediate layer material hardness, and  (2)core surface hardness−core center hardness (JIS-C)≧11.  (3)
 2. Themulti-piece solid golf ball of claim 1, wherein the core, envelopelayer, intermediate layer and cover have hardnesses which satisfy therelationshipcore surface hardness≦envelope layer surface hardness<intermediate layermaterial hardness>cover material hardness.
 3. The multi-piece solid golfball of claim 1, wherein the resin material making up the envelope layeris a mixture comprising, in admixture, a base resin of (a) anolefin-unsaturated carboxylic acid random copolymer and/or a metal ionneutralization product of an olefin-unsaturated carboxylic acid randomcopolymer mixed with (b) an olefin-unsaturated carboxylicacid-unsaturated carboxylic acid ester ternary random copolymer and/or ametal ion neutralization product of an olefin-unsaturated carboxylicacid-unsaturated carboxylic acid ester ternary random copolymer in aweight ratio between 100:0 and 0:100, and (e) a non-ionomericthermoplastic elastomer in a weight ratio between 100:0 and 50:50. 4.The multi-piece solid golf ball of claim 1, wherein the resin materialmaking up the envelope layer is a mixture comprising: 100 parts byweight of a resin component composed of, in admixture, a base resin of(a) an olefin-unsaturated carboxylic acid random copolymer and/or ametal ion neutralization product of an olefin-unsaturated carboxylicacid random copolymer mixed with (b) an olefin-unsaturated carboxylicacid-unsaturated carboxylic acid ester ternary random copolymer and/or ametal ion neutralization product of an olefin-unsaturated carboxylicacid-unsaturated carboxylic acid ester ternary random copolymer in aweight ratio between 100:0 and 0:100, and (e) a non-ionomericthermoplastic elastomer in a weight ratio between 100:0 and 50:50; (c) 5to 80 parts by weight of a fatty acid and/or fatty acid derivativehaving a molecular weight of 280 to 1500; and (d) 0.1 to 10 parts byweight of a basic inorganic metal compound capable of neutralizingun-neutralized acid groups in the base resin and component (c).
 5. Themulti-piece solid golf ball of claim 1, wherein the resin materialmaking up the cover is a material composed primarily of a heated mixtureof (A) a thermoplastic polyurethane material, and (B) an isocyanatemixture of (b-1) an isocyanate compound having at least two isocyanategroups as functional groups per molecule, dispersed in (b-2) athermoplastic resin which is substantially non-reactive with isocyanate.6. The multi-piece solid golf ball of claim 1, wherein the core materialis composed of, in admixture, a rubber base, sulfur and an organosulfurcompound.
 7. The multi-piece solid golf ball of claim 1, wherein theenvelope layer, intermediate layer and cover have thicknesses whichsatisfy the relationship:cover thickness<intermediate layer thickness≦envelope layer thickness.8. The multi-piece solid golf ball of claim 1, wherein the core hashardness which satisfy the relationshipcore surface hardness−core center hardness (JIS-C)≧15.
 9. Themulti-piece solid golf ball of claim 1, wherein the core has hardnesswhich satisfy the relationshipcore surface hardness−core center hardness (JIS-C)≧20.
 10. Themulti-piece solid golf ball of claim 1, wherein the diameter of the coreis 31 to 34.96 mm.
 11. The multi-piece solid golf ball of claim 1,wherein the number of the dimples is at least 280 but not more than 360.12. The multi-piece solid golf ball of claim 1, wherein the number ofthe dimples is at least 300 but not more than
 350. 13. The multi-piecesolid golf ball of claim 1, wherein the diameter of the dimples is setto at least 2.5 mm but not more than 6.5 mm.
 14. The multi-piece solidgolf ball of claim 1, wherein the depth of the dimples is set to atleast 0.08 mm but not more than 0.30 mm.
 15. The multi-piece solid golfball of claim 1, wherein the dimple coverage on the spherical surface ofthe golf ball, which is the sum of the individual dimple surface areas,each defined by the border of the flat plane circumscribed by the edgeof a dimple, expressed as a ratio (SR) with respect to the sphericalsurface area of the ball were it to be free of dimples, is at least 60%but not more than 90%.
 16. The multi-piece solid golf ball of claim 1,wherein the value V0 obtained by dividing the spatial volume of eachdimple below the flat plane circumscribed by the edge of that dimple bythe volume of a cylinder whose base is the flat plane and whose heightfrom the base to the maximum depth of the dimple is at least 0.35 butmore than 0.80.
 17. The multi-piece solid golf ball of claim 1, whereinthe VR value, which is the sum of the volumes of individual dimplesformed below flat planes circumscribed by the dimple edges, as apercentage of the volume of the ball sphere were it to have no dimplesthereon, is at least 0.6% but not more than 1.0%.
 18. The multi-piecesolid golf ball of claim 1, wherein the intermediate layer material iscomposed primarily of, in admixture, both a zinc-neutralized ionomerresin and a sodium-neutralized ionomer resin in which the mixing ratio,expressed as the weight ratio of zinc-neutralized resin tosodium-neutralized resin is from 25/75 to 75/25.
 19. A multi-piece solidgolf ball comprising a core, an envelope layer encasing the core, anintermediate layer encasing the envelope layer, and a cover whichencases the intermediate layer and has formed on a surface thereof aplurality of dimples, wherein the core is made primarily of a rubbermaterial and has a diameter of at least 31 mm, the envelope layer andintermediate layer are each made primarily of the same or differentresin materials and the cover is made primarily of polyurethane, thematerial hardness of the cover is softer than the material hardness ofthe intermediate layer by the hardness difference of at least 1 but lessthan 40 in Durometer D hardness units; the envelope layer, intermediatelayer and cover have thicknesses which satisfy the relationshipcover thickness<intermediate layer thickness≦envelope layer thickness;and the core, envelope layer, intermediate layer and cover have hardnessrelationships which satisfy the following three conditions:cover material hardness<intermediate layer material hardness, and  (2)core surface hardness−core center hardness (JIS-C)≧11.  (3)
 20. Themulti-piece solid golf ball of claim 19, wherein the resin materialmaking up the envelope layer is a mixture comprising, in admixture, abase resin of (a) an olefin-unsaturated carboxylic acid random copolymerand/or a metal ion neutralization product of an olefin-unsaturatedcarboxylic acid random copolymer mixed with (b) an olefin-unsaturatedcarboxylic acid-unsaturated carboxylic acid ester ternary randomcopolymer and/or a metal ion neutralization product of anolefin-unsaturated carboxylic acid-unsaturated carboxylic acid esterternary random copolymer in a weight ratio between 100:0 and 0:100, and(e) a non-ionomeric thermoplastic elastomer in a weight ratio between100:0 and 50:50.
 21. The multi-piece solid golf ball of claim 19,wherein the resin material making up the envelope layer is a mixturecomprising: 100 parts by weight of a resin component composed of, inadmixture, a base resin of (a) an olefin-unsaturated carboxylic acidrandom copolymer and/or a metal ion neutralization product of anolefin-unsaturated carboxylic acid random copolymer mixed with (b) anolefin-unsaturated carboxylic acid-unsaturated carboxylic acid esterternary random copolymer and/or a metal ion neutralization product of anolefin-unsaturated carboxylic acid-unsaturated carboxylic acid esterternary random copolymer in a weight ratio between 100:0 and 0:100, and(e) a non-ionomeric thermoplastic elastomer in a weight ratio between100:0 and 50:50; (c) 5 to 80 parts by weight of a fatty acid and/orfatty acid derivative having a molecular weight of 280 to 1500; and (d)0.1 to 10 parts by weight of a basic inorganic metal compound capable ofneutralizing un-neutralized acid groups in the base resin and component(c).
 22. The multi-piece solid golf ball of claim 19, wherein the resinmaterial making up the cover is a material composed primarily of aheated mixture of (A) a thermoplastic polyurethane material, and (B) anisocyanate mixture of (b-1) an isocyanate compound having at least twoisocyanate groups as functional groups per molecule, dispersed in (b-2)a thermoplastic resin which is substantially non-reactive withisocyanate.
 23. The multi-piece solid golf ball of claim 19, wherein thecore material is composed of, in admixture, a rubber base, sulfur and anorganosulfur compound.
 24. The multi-piece solid golf ball of claim 19,wherein the core has hardness which satisfy the relationshipcore surface hardness−core center hardness (JIS-C)≧15.
 25. Themulti-piece solid golf ball of claim 19, wherein the core has hardnesswhich satisfy the relationshipcore surface hardness−core center hardness (JIS-C)≧20.
 26. Themulti-piece solid golf ball of claim 19, wherein the core and envelopelayer have hardnesses which satisfy the relationshipcore surface hardness≦envelope layer surface hardness.
 27. Themulti-piece solid golf ball of claim 19, wherein the diameter of thecore is 31 to 34.96 mm.
 28. The multi-piece solid golf ball of claim 19,wherein the number of the dimples is at least 300 but not more than 350;the diameter of the dimples is set to at least 2.5 mm but not more than6.5 mm; the depth of the dimples is set to at least 0.08 mm but not morethan 0.30 mm; the dimple coverage on the spherical surface of the golfball, which is the sum of the individual dimple surface areas, eachdefined by the border of the flat plane circumscribed by the edge of adimple, expressed as a ratio (SR) with respect to the spherical surfacearea of the ball were it to be free of dimples, is at least 60% but notmore than 90%; the value V0 obtained by dividing the spatial volume ofeach dimple below the flat plane circumscribed by the edge of thatdimple by the volume of a cylinder whose base is the flat plane andwhose height from the base to the maximum depth of the dimple is atleast 0.35 but more than 0.80; the VR value, which is the sum of thevolumes of individual dimples formed below flat planes circumscribed bythe dimple edges, as a percentage of the volume of the ball sphere wereit to have no dimples thereon, is at least 0.6% but not more than 1.0%.29. The multi-piece solid golf ball of claim 19, wherein theintermediate layer material is composed primarily of, in admixture, botha zinc-neutralized ionomer resin and a sodium-neutralized ionomer resinin which the mixing ratio, expressed as the weight ratio ofzinc-neutralized resin to sodium-neutralized resin is from 25/75 to75/25.